Wuchang Pigment has been engaged in the production, R&D and sales management team of high performance iron oxide series products for more than 20 years. The senior managers are all from domestic Iron oxide pigments production enterprises. At present, there are more than ten high-performance iron oxide inventions. The high-temperature resistant zinc iron yellow, coated iron yellow, ferromanganese black, low arsenic red and red pigments for lithium batteries have been produced in large quantities. At the same time, the food-grade products developed by the company have passed strict European Union testing, and all heavy metal indicators are superior to industry and food-grade control standards.purposeHigh temperature resistance is generally used in plastics, PPC, PPE and other plastic products, wood plastic, aircraft shell, various plastics, thermosetting plastics, thermoplastic, rubber products, tires, coatings, etc.(High-temperature Resistant Grade Iron Oxide) | | |
Color | Type | Temperature resistance | [Fe2O3(105ºC Fe2O3 (Drying at 105ºC) | Volatile at 105°C | )Water soluble matter(Hot extraction method) | Residue(45um) | pH value | Oil absorption (g/100g) | Heat resistant to 30min | Tinting strength(Compared with standard) | |
Zinc iron yellow | 3950T | 800° | ≥65.0% | ≤0.5% | ≤0.5% | ≤0.3% | 5.0-8.0 | 25-35 | ΔE≤2(800ºC) | 95%-105% | |
Coated iron yellow | BM313 | 300° | ≥65.0% | ≤0.5% | ≤0.5% | ≤0.3% | 5.0-8.0 | 25-35 | ΔE≤2(300ºC) | 95%-105% | |
Ferromanganese black | 770T | 700° | ≥65.0% | ≤0.5% | ≤1.5% | ≤0.3% | 5.0-8.0 | 20-30 | ΔE≤2(700ºC) | 95%-105% | |
Coated iron oxide red | BM130 | 700° | ≥85% | ≤0.5% | ≤1.5% | ≤0.3% | 5.0-8.0 | 20-30 | ΔE≤2(700ºC) | 95%-105% | |
Contact us if you need more details on Iron Oxide Yellow. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Iron Oxide Green、Iron Oxide Pigments. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Iron oxide pigments > High temperature resistant iron oxide pigments